Gate Valve Seat Supplier

본문 바로가기


Home > Product > Gate Valve Seat Supplier
Product
Gate Valve Seat Supplier
Posting date : Aug 12, 2019
Membership
Free Member Scince Sep 30, 2018
FOB Price
-
Min. Order Quantity
100 sets
Supply Abillity
40000 sets per year
Port
Shanghai
Payment Terms
Prepaid 30% deposit, 70% to delivery.
Package
wooden case
Keyword :
Category
Contact
Aaron
          0 likes     
Product Detail
Company Info
 
Quick Detail
Place of Origin
China [CN]
Brand Name
kaitianfu
HS-CODE
-
Package & Delivery Lead Time
Package
wooden case
Delivery Lead Time
60 days
Detailed Description
COMMON Valve Seat Coating MATERIALS
Valve Seat: The detachable surface parts in valve are used to support the valve spool in the fully closed position and constitute a sealed part. Generally, valve seat diameter is the maximum flow diameter of the valve.
PRODUCT PARAMETERS FOR OUR high performance valve seat
This part can be illustrated by a table shown below:
 
name
Description
Chemical composition
Max thickness
Hardness
Bond strength
Porosity
Limit temperature
Costing
characterlzation
wt.%
mm
HV0.3
MPa
%
WC-CoCr
WC86/Co10/Cr4
Co:9-11
Cr:3.5-4.5
C:3.5-4.5
W: Bal
1
1100-1500
>75
<1%
482
 Good abrasive resistance at low temperature
 Compared with WC-Co, its oxidation resistance 
and corrosion resistance are improved.
 The coating is compact and hard
WC-Co
WC88/Co12
Co:11-13
C:3.6-5.5
W:Bal
2
1050-1200
>75
<1%
454
 Good abrasive resistance at low temperature.
 Limited oxidation resistance and corrosion 
resistance.
 The coating is compact and hard.
WC-Co
WC83/Co17
Co:16-18
C:4.8-5.5
W: Bal
2
950-1100
>75
<1%
454
 Good abrasive resistance at low temperature.
 Compared with WC-12Co, its abrasive resistance 
is poor, but toughness, impact strength and ductility are better.
 The coating is compact and hard.
Cr3C2 -NiCr
75Cr3C2 /25NiCr
Ni:16-21C:9-11
Cr:11
B:2.2 
Si:4 
Fe:2.7
C:0.4
Ni:Bal
1
750-900
>75
<1.5%
871
 Good abrasive and sliding abrasive performance 
of abrasive-resistant materials at high temperatures.
 Good corrosion resistance.
Cr3C2 -NiCr
80Cr3C2 /20NiCr
Ni:14-18
C:9-11
Cr:Bal
1
800-950
>75
<1.5%
871
 Good abrasive and sliding abrasive performance 
of abrasive-resistant materials at high temperatures.
 Good corrosion resistance.
CoCrW   Alloy
Stellite 6
Cr:29
W:4
Ni:3
Fe:3
C:1.15
Si:1.1
Co:Bal
0.6
HRC38±5
>55
<2%
649
 Thermosetting and abrasive resistance are good.
 Oxidation resistance and corrosion resistance 
are good.
CoCrW Alloy
Stellite 12
Cr:29.5
W:8.25
Ni:3
Fe:3
C:1.4
Si:1.45
Co:Bal
0.6
HRC42±5
>55
<2%
649
 Thermosetting and abrasive resistance are good. 
Compared with 6#, its abrasive resistance is better.
 Oxidation resistance and corrosion resistance are 
good.
CoCrW Alloy
Stellite 20
Cr:32.5
W:17.5
Ni:3
Fe:3
C:2.45
Si:1.0
Co:Bal
0.6
HRC52±5
>55
<2%
649
 Thermosetting and abrasive resistance are good. 
Compared with 12#, its abrasive resistance is 
better.
 Oxidation resistance and corrosion resistance are good.
Nickel   Alloy
Ni50
Cr:11
B:2.2
Si:4
Fe:2.7
C:0.4
Ni:Bal
0.5
HRC50±5
>41(HVOF)
<2%
550
 Stand wear and tear
 Erosion and abrasion
 Machinable
Nickel   Alloy
Ni55
Cr:15.5
B:3.0
Si:4
Fe:14
Mo:3
C:0.75
Ni:Bal
0.5
HRC55±5
>41(HVOF)
<2%
550
 Stand wear and tear
 Erosion and abrasion
 Machinable

ECROBOT CO., Ltd, Business Registration Number : 220-88-71747, CEO J.W.Park, TEL : +82-2-552-7676, E-mail : E-mail : Contact us
Address : (Hwanghwa B/D 11F, Yeoksam-dong)320, Gangnam-daero, Gangnam-gu, Seoul, South Korea
About Us Privacy Policy Terms of use Copyright © 2000-2024 ECROBOT.COM. All rights reserved.
Top