Tests
|
Value
|
Unit
|
Melt Flow Rate (MFR)
|
1
|
g/10min
|
Density
|
0.922
|
g/cm3
|
Tensile Yield Strength
|
7
|
Mpa
|
Elongation at Break
|
75
|
%
|
Wien Softening Point
|
85
|
°C
|
Packing
|
In 25 kg PP woven bags,20MT/20’FCL
|
Tests
|
Value
|
Unit
|
Melt Flow Rate (MFR)
|
2
|
g/10min
|
Density
|
0.9225
|
g/cm3
|
Tensile Strength
|
9
|
Mpa
|
Elongation at Break
|
500
|
%
|
Fish eye max(0.3-2mm)
|
30
|
n/1200cm2
|
Stripes
|
20
|
cm/20m3
|
Packing
|
In 25 kg PP woven bags,20MT/20’FCL
|
ITEM
|
Unite
|
Value
|
Test Method
|
Density
|
g/cm3
|
0.919
|
GB/T 1033
|
Melt Mass-Flow Rate
(MFR, 2.16kg)
|
g/10 min
|
1.5
|
GB/T 3682
|
Fish Eye 0.3mm-2mm
|
n/1200cm3
|
2
|
GB 11115
|
Haze
|
%
|
24
|
GB/T 2410
|
Tensile Strength at Yield
|
MPa
|
12.5
|
GB/T 1040
|
Elongation at Break
|
%
|
550
|
GB/T 1040
|