Plastic PVC Resin
China [CN]
|
Item No. |
SG 5 |
|
K Value |
68-66 |
|
Viscosity ml/g |
118-107 |
|
Average Polymerization |
1100-1000 |
|
Number of impurity particles |
≤30 |
|
Volatile Content(incl.water)% |
≤0.40 |
|
Apparent Density g/ml |
≥0.45 |
|
Residual After Sieve 0.25mm mesh |
≤2.0 |
|
Number of Grain/400cm2 |
≤40 |
|
Plasticizer Absorption of 100g Resin |
≥20 |
|
Whiteness(160,after 10 min)% |
≥80 |
|
VCM Residue PPM |
≤3 |
|
Ethylidene Chloride mg/kg |
≤150 |
|
Packaging |
25 Kgs/Bag |
|
MOQ |
16TON(1*20FCL) |
|
Payment terms |
30% advance |
|
70% see the B/L copy pay the |
| Tape: | SG1 | SG2 | SG3 | SG4 | SG5 | SG6 | SG7 | SG8 |
| K value | 77-75 | 74-73 | 72-71 | 70-69 | 68-66 | 65-63 | 62-60 | 59-55 |
| Viscosity, ml/g | 156-144 | 143-136 | 135-127 | 126-119 | 118-107 | 106-96 | 95-87 | 86-73 |
| Average polymerization | 1350-1250 | 1250-1150 | 1100-1000 | 950-850 | 950-850 | 750-650 | ||
| Number of impurity particle≤ | 30 | 30 | 30 | 30 | 30 | 30 | 40 | 40 |
| Volatiles content %,≤ | 0.40 | 0.40 | 0.40 | 0.40 | 0.40 | 0.40 | 0.40 | 0.40 |
| Appearing density g/ml≥ | 0.42 | 0.42 | 0.42 | 0.42 | 0.42 | 0.45 | 0.45 | 0.45 |
| Residual after sieve 0.25mm mesh≤ | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 | 2.0 |
| 0.063mm l≥ | 90 | 90 | 90 | 90 | 90 | 90 | 90 | 90 |
| Number ofgrain/400cm2≤ | 40 | 40 | 40 | 40 | 40 | 40 | 40 | 40 |
| Plasticizer absorbency value of 100g resin | 25 | 25 | 25 | 22 | 19 | 16 | 14 | 14 |
| Whiteness %,≥ | 74 | 74 | 74 | 74 | 74 | 74 | 70 | 70 |
| Residual chlore thylene content mg/kg≤ | 5 | 5 | 5 | 5 | 5 | 5 | 5 | 5 |
| Ethylidene chloride mg/kg≤ | 150 | 150 | 150 | 150 | 150 | 150 | 150 | 150 |
Click enlarge Image